What's your feeling about adding H2O2 to CS after it has aged a few days?

Dan

On Sun, Mar 5, 2017 at 8:05 AM, Ode Coyote <silverpuppy1...@gmail.com>
wrote:

> Never never use salt in a batch of CS.
> H202 will boost the formation of silver 'particles' so much so that
> conductivity may never rise [no increase in current draw].
> Those silver particles have no charge and will eventually grow so large
> that they will settle out as shiny metal flakes, later oxidized by excess
> H2O2 into fuzzy black silver oxide balls and deep yellow liquid.
>
> If you want to keep using H2O2 while making CS, use 3 or less drops of 3%
> per quart
>
> Ode
>
> Ode
>
> On Sat, Mar 4, 2017 at 11:19 PM, <glendajma...@aol.com> wrote:
>
>>
>>
>>
>> I am having a problem, that did not manifest before.
>> I have made colloidal silver before, 1 quart jar, distilled water, tsp of
>> h202, 18 volts dc.
>> I would see a gray cloud form in the jar, before...
>>
>> I started up again, but this time no gray cloud from the electrode.
>> ???
>> could it be the h202 is different in this case, can't think of anything
>> else.
>> If I put a pinch of salt I will get the cloud, but now all I get is o2
>> bubbles clustering on one electrode after
>> 40 minutes?????
>>
>>                                            What am I doing differently,
>> that I am not aware of, or is this better
>>                                                now than before??
>>
>>                                                      Glenda
>>
>
>