I don't know what solder it uses, but it doesn't matter. You ADD some more of the lower temp solder, so that the mix becomes low temp melt, and then do your soldering work. You can buy some REALLY low temp solder and use that for the removal. (Chip Quik has one, but there are others also.) Then clean things well from the low temp stuff and use regular solder to put things back on.
Unless your soldering iron is simply not working up to snuff and even with this trick won't get warm enough, and then?? I haven't yet met a solder that the Hakko won't melt. On Fri, May 15, 2026 at 4:01 PM King Beowulf <[email protected]> wrote: > Hello PLUGgers, > > Not really a Linux/Unix question, but since some of you have experience > in the electronics biz, maybe you have some ideas. > > I have a GPU with a blower style heat sink and fan (single fan, Cu block) > > Zotac Gaming Geforce RTX 3090 > > Since the blower is a bit loud (it was a data center GPU once upon a > time), after some research I found the "desktop" version of the fan / > heat sink - a standard Al heat pipe with 3 fans, as is used for most > gaming GPU. This heat sing/triple fan does fit, but I need to make a > slight modification. > > Blower type cards typically have the 2 power connectors on the end of > the PCB J5010, J5011 - as this one does - and I just need to move the > connectors to the top PCB edge J1 and J2 locations so that the heat sink > /fan and shroud will line up and fit. > > Since my old Weller WP25 soldering iron tops out at 250C, and is showing > it age a bit (bought it ? decades ago), I splurged on a > > Hakko FX888DX-010BY - Digital Soldering Station > > 50-480C > 65W ceramic heater > chisel, 1.6 mm tip > > Now, most of my fiddling involves Sn/Pb, Sn/Ag/[Cu,Bi,Se] solders at > 250-350C, and the Hakko wand has no problems liquefying these. However, > I am not able to melt to remove the solder from the GPU PCB connectors, > even at a setting of 400-480C. > > Does anyone have any ideas or information on the solder used on GPU PCBs > and components? > > -Ed > > > > >