Dear All
I would like to grow UO2 thin films on STO (SrTiO3) substrate but I found that
Sr K-edge 16105 and U L3-edge is 17166. Do you think there will be any
interference?
Best,
Mohamed
___
Ifeffit mailing list
Dear
I would like to fit the signal from (U0.8Ce0.2)O2, so I tried to put Ce in the
same position of U but all atoms generated files give no Ce in the scattering
paths and some fitting give negative amplitude values. Could you help me with
the Atoms input file?
Mohamed
- Forwarded Message
From: mohamed sobhy bakhshwan1...@yahoo.com
To: ifeffit@millenia.cars.aps.anl.gov
Sent: Thu, May 20, 2010 4:14:18 PM
Subject: [Ifeffit] fitting
Dear all thanks for your help and explanation about the background
I
fitted my data after removing the background
Dear all thanks for your help and explanation about the background
I
fitted my data after removing the background and in the attached file I
got this fitting, although all the values are good but I think the coordination
number should be less than 8 (for the first shell) due to irradiation.
So
Dear all
I am trying to use artemis to do fitting to CeO2. But really I cant get the
right way to do that.
During the fitting, I am using amp as set and change in N degeneracy of the
path. attached is the best fit i got but it still not good and the chi-square
is 41.109065479
so can you
Dear all
I am trying to fit some data of coordination number 8, but I always find the
fitting of the first shell give the coordination number only about 0.5.
I
do not know what is wrong. Do I need to fit first and second and third
shells altogether, and if that is right how Can I do that??