Agree. Took a quick look at your spectrum. The IrOx seems to be extremely
amorphous without much Ir-Ir interactions. The dip is around 11 (A-1) in
the k-space. So you may just truncate anything beyond that dip and the
remaining spectrum should carry most useful information and be fitable, at
least
Hi Kavya:
What you have are not glitches but shifts in the absolute absorption
probably due to bubbles or droplets moving through the beam. You can tell
these from crystal glitches because the glitches are sharp and occur at the
same energy in every scan while these are likely to move around