Hi Yordy:
I'm sorry. The xdp module is one that was written here by my group to
provide I/O for data files produced at our beamline. I have packaged it
for Debian but it is not out there for the general public yet. In the
program I sent you the xdp module is only used to write out the
Hi all,
I am working with Er doped ZnO and the EXAFS measurements (Er L3) shows that
I have not a second shell when I perform the FT. I checked that the phase is
not destroying the signal, and that is not the guilty guy.
I have two possibilities, that the erbium is segregated on the surface of
the
Eugenio,
The possibilities depend on the actual data at hand. Not seeing second shell is
a relative term. Do you mean that you do not see it above noise? Then,
technically, you cannot say that you do not have a second shell. Er may
substitute for Zn and you will still have Er-Zn