> ...I had to look up "work hardening," but that sure makes sense. I did > notice that the cracked line when removed had little or no give,.. > I could have clarified that the tube will break off in a fitting that is not vibrating. I have to say that in my case it was a copper line but I would think aluminum would be subject to the same failure although perhaps in a different number of bending cycles.