I also strongly support Armel Le Bail viewpoint about the coherent
diffracting domains or coherently scattering regions. This is what is
measured with this method. Coherently scattering regions maybe much
smaller (sometimes several orders of magnitude) than the grain size.
Unfortunately there is a
Hello Doinita,
It might be that you have some order in the occupancies of V,
O and vacancies. Did you check for this possibility?
Rosa Barabash
From: Doinita E Neiner
[mailto:[EMAIL PROTECTED]
Sent: Friday, November 05, 2004
5:53 PM
To: [EMAIL PROTECTED]
Subject: partial
Hi,
One should be careful with interpretation of anisotropic line
broadening. Anisotropic line broadening can be due to the formation of
small dislocation loops, dipoles or some early stages of
pre-precipitation (GP zones) in the alloy.
Would be nice if you can obtain information about