Following are the results of colloidal silver solution preparation made on
January 26, 1998:
SAMPLE SAMPLE SAMPLE
A2X B1Y
C3Z
1. ounces of boiled,distilled water: 8 6
6
2. ounces of starter solution: 8 2
2
3. duration of process (minutes): 18 10 11
4. ambient (room) temp in
degrees Fahrenheit: 77 77
77
5. weather: sunny sunny
sunny
6. electrode separation (inches): 3/8 1/2 3/8
7. temperature in degrees
Fahrenheit of water that bottle
is placed in: 170 170
172
8. approx. time of day (p.m.) 2:30 3:00 3:30
9. number of times electrodes
cleaned: 3 1
2
10. color of final solution: golden, golden,
golden,
light medium
medium
11. ppm as measured by
Aqualab, Tucson, AZ: 25 34
36
Notes:
a. Sample A2X was the starter solution.
b. The lower half of the bottle containing the colloidal silver solution was
placed in a pan of heated water. The water was heated over a natural gas
burner.
c. The electrodes (99.99% pure) used were those supplied by Action
Electronics.
d. The electrodes were approxately 90% covered by the colloidal silver
solution.
e. Electrode separation was measured at the end of the electrodes. The
electrode separation at the beginning was about 1/8 inches.
Hope that the above information helps in our research.
Harry Davis
--
The silver-list is a moderated forum for discussion of colloidal silver.
To join or quit silver-list or silver-digest send an e-mail message to:
[email protected] -or- [email protected]
with the word subscribe or unsubscribe in the subject: line.
To post, address your message to: [email protected]
List maintainer: Mike Devour <[email protected]>