If you have suspended silver oxides [yellow batch] 3 to 6 drops of peroxide/quart or Liter will clear it up...but wait a few days before doing that or it will make it worse. Otherwise, why bother?
A bit of peroxide 'under power' does different than adding it later. ode On Sun, Mar 5, 2017 at 3:04 PM, Dan Nave <bhangcha...@gmail.com> wrote: > What's your feeling about adding H2O2 to CS after it has aged a few days? > > Dan > > On Sun, Mar 5, 2017 at 8:05 AM, Ode Coyote <silverpuppy1...@gmail.com> > wrote: > >> Never never use salt in a batch of CS. >> H202 will boost the formation of silver 'particles' so much so that >> conductivity may never rise [no increase in current draw]. >> Those silver particles have no charge and will eventually grow so large >> that they will settle out as shiny metal flakes, later oxidized by excess >> H2O2 into fuzzy black silver oxide balls and deep yellow liquid. >> >> If you want to keep using H2O2 while making CS, use 3 or less drops of 3% >> per quart >> >> Ode >> >> Ode >> >> On Sat, Mar 4, 2017 at 11:19 PM, <glendajma...@aol.com> wrote: >> >>> >>> >>> >>> I am having a problem, that did not manifest before. >>> I have made colloidal silver before, 1 quart jar, distilled water, tsp >>> of h202, 18 volts dc. >>> I would see a gray cloud form in the jar, before... >>> >>> I started up again, but this time no gray cloud from the electrode. >>> ??? >>> could it be the h202 is different in this case, can't think of anything >>> else. >>> If I put a pinch of salt I will get the cloud, but now all I get is o2 >>> bubbles clustering on one electrode after >>> 40 minutes????? >>> >>> What am I doing differently, >>> that I am not aware of, or is this better >>> now than before?? >>> >>> Glenda >>> >> >> >