Question #697548 on Yade changed:
https://answers.launchpad.net/yade/+question/697548
Status: Needs information => Open
Du Zhang gave more information on the question:
Hi Jan Stránský,
thank you very much for your reply and suggestions! I would like to add
more information.
The single sand grain will be simulated as an agglomerate ( a group of
sub-particles bonded together ). This agglomerate will be loaded between
two steel plates with a small constant load for days or months. Time-
dependent fracturing/deformation/force at contacts can be simulated.
Is there the Parallel-Bonded Stress Corrosion (PSC) model or any other similar
model in Yade?
PSC model was proposed by Potyondy (2007) as an extension of BPM to include the
time-dependent behavior of rocks (the time-dependent development of
microcracks) by adding a damage-rate law to the parallel-bond formulation. If a
parallel bond is under tensile stress higher than the activation stress, the
bonding material will be removed at a specified rate governed by a damage-rate.
I found a class yade.wrapper.CpmMat. It has "damLaw" for damage
evolution in uniaxial tension. I do not know if it is can reach my
object. Could you give me some advices? Thanks a lot again.
best,
Du Zhang
--
You received this question notification because your team yade-users is
an answer contact for Yade.
_______________________________________________
Mailing list: https://launchpad.net/~yade-users
Post to : [email protected]
Unsubscribe : https://launchpad.net/~yade-users
More help : https://help.launchpad.net/ListHelp