Hi from Joe: Re Duncan's request for volunteers - I'm a retired B.S. Electronics Eng'r; have the time, interest, most of the tools [my scope goes to 35 MHz - way short for RF nowdays] & have been wanting a Rife device for about 7 yrs but wouldn't afford $2 K. Don't know if it's other than chance but found http://cat007.com last night [from another egroup], was up till 4am digesting several pieces regarding Rife & CS. Have attempted to raise several who are familiar w EMEMR3D but had no response; seen vague descriptions but no real detail other than it has a phantatron [sp] tube for plasma generation. For those of you who haven't checked yet there is a file set under 'Your PC= Machine ... ' about 3/4 down the menu that gets to ' http://cat007.com/rife1.htm ' headed 'Thr Cancer Cure that Worked' [sic]. This file appears to be what I've been waiting yrs for - at the end there is a link to a 32 p. list of over 1200 entries w about 825 separate diseases, each listing from 1 f. to 2 lines of frequencies for that entry, ranging from 2.0 to 37000 Hz. There is a link to download the software [freeware] to use the two bit bell output on the CPU board [which needs a mod to run an external audio amp, hardly any detail] & nothing about connecting to yourself.
The file '.com/rife.htm mentions Rev. Wayne, Jack Nicklaus & others who use another Rife machine; some data about coupling there, but again, no detail. The above indicates that Finally, I could have 1 for about $100 + lots of aggravation getting it alive. Anyone who is Rife prone should check the above. Re CS - there is a file on the site above at http://cat007.com/silver.htm which is the main reason for this post. Since I've only been making CS for about 2 mo there was a statement about particle size that might explain some of my troubles w cloudy sol'n & suspect effectiveness. To successfully attack viruses, the particle size must be on the order of 10 - 25 nanometer, that of the commercially produced & marketed, none were really effective since their particle size was 40 & +; to get it he used less than 1/2 mA during the electrolysis & quit at about 5 ppm, no priming mentioned, initial current of about .01 mA [as mine did], had uncomplimentary words for claims above 100 ppm. He also stated that it was required that a [fish tank] pump be run & air be bubbled thru the mix while current is applied. Said his method gets clear mix in 5 hrs w no heating from a 6 Vdc supply [that will ordinarily run at about 8 - 9 V with that small a current load]. The biggest puzzle to me was the statement that forced air caused a combination of oxygen in the air to form CO2, increased from the typical amounts by the forced air, that it made eminent sense to the chemist he talked to [but not me] besides suppressing clumping. I noticed clumping when my sol'ns were in the startup stage at about 1 mA [& went to 15 mA at end portion] but didn't recognise it as a [fatal] problem. When I checked the sensitivity of my laser against a commercial bottle of 500 ppm CS, it showed very large particles still in suspension too, so didn't think anything suspicious [since I had no size range numbers then]. There may also be a trick about electrode spacing. He recommends Ag coins [.9999 Canadian Maple Leafs] be clamped to the opposite top edges of the 8 oz glass w the supply clip leads. I've been using about a 1/2 " spacing to increase the current during startup & found that it tends to short w conductive crud after midway thru. So, what can you experts advise me? Thanks. Bye. -- The silver-list is a moderated forum for discussion of colloidal silver. To join or quit silver-list or silver-digest send an e-mail message to: [email protected] -or- [email protected] with the word subscribe or unsubscribe in the SUBJECT line. To post, address your message to: [email protected] Silver-list archive: http://escribe.com/health/thesilverlist/index.html List maintainer: Mike Devour <[email protected]>
