Sent: Thursday, June 19, 2008 9:17 PM
Subject: Re: [MBZ] bending steel pipe
Tom Hargrave [EMAIL PROTECTED] writes:
You will not be able to completely straighten the pipe by hand.
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let it cool naturally
@okiebenz.com
Sent: Thursday, June 19, 2008 9:17 PM
Subject: Re: [MBZ] bending steel pipe
Tom Hargrave [EMAIL PROTECTED] writes:
You will not be able to completely straighten the pipe by hand.
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let
You will not be able to completely straighten the pipe by hand.
Thanks,
Tom Hargrave
www.kegkits.com
256-656-1924
-Original Message-
From: [EMAIL PROTECTED] [mailto:[EMAIL PROTECTED]
On Behalf Of Allan Streib
Sent: Thursday, June 19, 2008 8:06 PM
To: mercedes@okiebenz.com
Subject: [MBZ]
Tom Hargrave [EMAIL PROTECTED] writes:
You will not be able to completely straighten the pipe by hand.
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let it cool naturally. Or will it make any difference?
Allan
--
1983 300D
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let it cool naturally. Or will it make any difference?
Quenching it will harden it, to whatever point the steel is
capable of being hardened. Letting it air-cool will not (so
much). Don't know if this is an
- Original Message -
From: Allan Streib [EMAIL PROTECTED]
To: Mercedes Discussion List mercedes@okiebenz.com
Sent: Thursday, June 19, 2008 9:17 PM
Subject: Re: [MBZ] bending steel pipe
Tom Hargrave [EMAIL PROTECTED] writes:
You will not be able to completely straighten the pipe by hand
]
On Behalf Of Jim Cathey
Sent: Thursday, June 19, 2008 8:30 PM
To: Mercedes Discussion List
Subject: Re: [MBZ] bending steel pipe
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let it cool naturally. Or will it make any difference?
Quenching it will harden
Allan Streib wrote:
Assuming I can straighten it to my satisfaction, should I then dunk it
in water, or let it cool naturally. Or will it make any difference?
I'd put it in v blocks in a press and straighten it cold.
___
http://www.okiebenz.com
For new