Re: CS>CAN'T UNDERSTAND WHAT'S GOING ON WITH MY FORMULATION?

[Ode Coyote]

If you have suspended silver oxides [yellow batch]  3 to 6 drops of
peroxide/quart or Liter will clear it up...but wait a few days before doing
that or it will make it worse.
Otherwise, why bother?

A bit of peroxide 'under power'  does different than adding it later.
ode

On Sun, Mar 5, 2017 at 3:04 PM, Dan Nave  wrote:

> What's your feeling about adding H2O2 to CS after it has aged a few days?
>
> Dan
>
> On Sun, Mar 5, 2017 at 8:05 AM, Ode Coyote 
> wrote:
>
>> Never never use salt in a batch of CS.
>> H202 will boost the formation of silver 'particles' so much so that
>> conductivity may never rise [no increase in current draw].
>> Those silver particles have no charge and will eventually grow so large
>> that they will settle out as shiny metal flakes, later oxidized by excess
>> H2O2 into fuzzy black silver oxide balls and deep yellow liquid.
>>
>> If you want to keep using H2O2 while making CS, use 3 or less drops of 3%
>> per quart
>>
>> Ode
>>
>> Ode
>>
>> On Sat, Mar 4, 2017 at 11:19 PM,  wrote:
>>
>>>
>>>
>>>
>>> I am having a problem, that did not manifest before.
>>> I have made colloidal silver before, 1 quart jar, distilled water, tsp
>>> of h202, 18 volts dc.
>>> I would see a gray cloud form in the jar, before...
>>>
>>> I started up again, but this time no gray cloud from the electrode.
>>> ???
>>> could it be the h202 is different in this case, can't think of anything
>>> else.
>>> If I put a pinch of salt I will get the cloud, but now all I get is o2
>>> bubbles clustering on one electrode after
>>> 40 minutes?
>>>
>>>What am I doing differently,
>>> that I am not aware of, or is this better
>>>now than before??
>>>
>>>  Glenda
>>>
>>
>>
>

Re: CS>CAN'T UNDERSTAND WHAT'S GOING ON WITH MY FORMULATION?

[Dan Nave]

What's your feeling about adding H2O2 to CS after it has aged a few days?

Dan

On Sun, Mar 5, 2017 at 8:05 AM, Ode Coyote 
wrote:

> Never never use salt in a batch of CS.
> H202 will boost the formation of silver 'particles' so much so that
> conductivity may never rise [no increase in current draw].
> Those silver particles have no charge and will eventually grow so large
> that they will settle out as shiny metal flakes, later oxidized by excess
> H2O2 into fuzzy black silver oxide balls and deep yellow liquid.
>
> If you want to keep using H2O2 while making CS, use 3 or less drops of 3%
> per quart
>
> Ode
>
> Ode
>
> On Sat, Mar 4, 2017 at 11:19 PM,  wrote:
>
>>
>>
>>
>> I am having a problem, that did not manifest before.
>> I have made colloidal silver before, 1 quart jar, distilled water, tsp of
>> h202, 18 volts dc.
>> I would see a gray cloud form in the jar, before...
>>
>> I started up again, but this time no gray cloud from the electrode.
>> ???
>> could it be the h202 is different in this case, can't think of anything
>> else.
>> If I put a pinch of salt I will get the cloud, but now all I get is o2
>> bubbles clustering on one electrode after
>> 40 minutes?
>>
>>What am I doing differently,
>> that I am not aware of, or is this better
>>now than before??
>>
>>  Glenda
>>
>
>

Re: CS>CAN'T UNDERSTAND WHAT'S GOING ON WITH MY FORMULATION?

[Ode Coyote]

Never never use salt in a batch of CS.
H202 will boost the formation of silver 'particles' so much so that
conductivity may never rise [no increase in current draw].
Those silver particles have no charge and will eventually grow so large
that they will settle out as shiny metal flakes, later oxidized by excess
H2O2 into fuzzy black silver oxide balls and deep yellow liquid.

If you want to keep using H2O2 while making CS, use 3 or less drops of 3%
per quart

Ode

Ode

On Sat, Mar 4, 2017 at 11:19 PM,  wrote:

>
>
>
> I am having a problem, that did not manifest before.
> I have made colloidal silver before, 1 quart jar, distilled water, tsp of
> h202, 18 volts dc.
> I would see a gray cloud form in the jar, before...
>
> I started up again, but this time no gray cloud from the electrode.
> ???
> could it be the h202 is different in this case, can't think of anything
> else.
> If I put a pinch of salt I will get the cloud, but now all I get is o2
> bubbles clustering on one electrode after
> 40 minutes?
>
>What am I doing differently,
> that I am not aware of, or is this better
>now than before??
>
>  Glenda
>