When...has to do with waiting a few days till after the conductivity of
the brew has stopped dropping.
After that point, then dripping some HP in, I've not noticed a further drop.
Cleaning black electrodes with HP has been around a long time.
The leap to clearing out color is more recent.
HP will both break silver oxide up...and ....eventually oxidize silver if
the HP is in high enough concentration, but that's a different form of
oxide [there are about 4 or 5 possible]
It's a matter of when, where, how much and how long.
Ode
At 06:48 AM 8/25/2009 -0700, you wrote:
I think The late " Ole Bob " had a lot to do with the testing of CS and
H202 mix ? I know I started using H202 to clean up off color CS aprox 8
years ago when I lived in PHX, AZ.
I worked with ole Bob several time and sent him samples of my CS. I know
if we look back in the archives you will find H202 discussions over and
over.I have had different results using the same methods. Some silver
will clean up great using H202, some gets worse.
Seems like it happens when there is a solar disturbance or
something? H202 is great for lowering the size of your Silver Atoms,
however it also lowers your measurable PPM with a TDS tester. But your
lower PPM CS is still effective for what it was intended.
Tel Tofflemire
Dewey, AZ.
---
--
The Silver List is a moderated forum for discussing Colloidal Silver.
Instructions for unsubscribing are posted at: http://silverlist.org
To post, address your message to: [email protected]
Address Off-Topic messages to: [email protected]
The Silver List and Off Topic List archives are currently down...
List maintainer: Mike Devour <[email protected]>