What Actual silver content is depends on who measures it and how, but...
I have made crystal clear LVDC CS up to and over 53PPM by Trems microsiemens x1.2 method of measurement which agrees somewhat with the lab testing at the NC State water laboratory...or about 30+ PPM by Ole Bobs photospectrometer. [The latest batch was made MUCH stronger than the batch he tested at 26.8 PPM, is still crystal clear with a bright and fine TE after several days]
Apparently keeping a fairly contant temperature in storage is important as the clear batch I sent to Ole Bob had turned a very faint yellow by the time it arrived while identical batches stay colorless here.
Last spring I split a batch between 2 bottles. One bottle left near an open window and subject to temperature shifts went yellow over night, the other half kept in the bathroom is still clear after several months.
Ken
At 09:52 PM 7/27/02 EDT, you wrote:
>>>>
In a message dated 7/27/2002 9:35:07 PM Eastern Daylight Time, [email protected] writes:<<<<
I have a LVDC generator which I use to produce 44oz batches -- each batch is clear,
and stays that way, until it is all gone - about 3 weeks.
To my understanding, it must be low PPM. The point I was trying to make is, hvac makes a strong product that is still clear. YOu can't do that with DC I don't think. Either way, it's the high voltage, sometimes 15000 volts, that causes a stronger bond and smaller particles. To my understanding.
What DC unit are you using? Maybe there is something I do not know and would like to. Thanks.
-- The silver-list is a moderated forum for discussion of colloidal silver.
Instructions for unsubscribing may be found at: http://silverlist.org
To post, address your message to: [email protected]
Silver-list archive: http://escribe.com/health/thesilverlist/index.html
List maintainer: Mike Devour <[email protected]>