If you have suspended silver oxides [yellow batch] 3 to 6 drops of
peroxide/quart or Liter will clear it up...but wait a few days before doing
that or it will make it worse.
Otherwise, why bother?
A bit of peroxide 'under power' does different than adding it later.
ode
On Sun, Mar 5, 2017 at
What's your feeling about adding H2O2 to CS after it has aged a few days?
Dan
On Sun, Mar 5, 2017 at 8:05 AM, Ode Coyote
wrote:
> Never never use salt in a batch of CS.
> H202 will boost the formation of silver 'particles' so much so that
> conductivity may never
Never never use salt in a batch of CS.
H202 will boost the formation of silver 'particles' so much so that
conductivity may never rise [no increase in current draw].
Those silver particles have no charge and will eventually grow so large
that they will settle out as shiny metal flakes, later
I am having a problem, that did not manifest before.
I have made colloidal silver before, 1 quart jar, distilled water, tsp of h202,
18 volts dc.
I would see a gray cloud form in the jar, before...
I started up again, but this time no gray cloud from the electrode.
???
could it be the